art photonics GmbH, founded in Berlin in September 1998, is one of the worldwide leaders in development and production of specialty fiber products for a broad spectrum from 300 nm to 16 µm. Unique technologies of Polycrystalline Mid InfraRed (PIR-) fibers and Metal coated Silica fibers are used for assembly of various spectroscopy probes for medical diagnostics and industrial process control, in volume production of fiber for medical and industrial lasers, for different fiber bundles, etc.
UV 200-400 nm
Visible
Near IR 750-2500 nm
Mid IR 2.5 - 18 µm

Polykristalline Infrarot-Fasern

Kategorien: , Schlagwort:

Eigenschaften:

  • Hoher Transmissionsgrad im Bereich 3 - 17 μm
  • Geringe optische Verluste von etwa 0,2 - 0,3 dB/m im Bereich 9 - 13 µm
  • Kern/Clad-Struktur mit Kerndurchmessern im Bereich von 240 bis 860 μm
  • Minimaler Alterungseffekt
  • Nicht hydroskopisch und nicht toxisch

Beschreibung

art photonics hat eine Serienproduktionstechnologie für ein einzigartiges Produkt entwickelt - Polykristalline Infrarotfasern (PIR-Fasern), die über einen breiten Spektralbereich von 3 bis 17 μm transparent sind.

Die leistungsfähigsten PIR-Kern/Mantel-Fasern werden mit Kerndurchmessern von 240µm bis 860µm extrudiert. Ein kontinuierlich verbessertes Extrusionsverfahren sorgt für eine hervorragende optische Qualität und mechanische Festigkeit der PIR-Fasern.

Geringe optische Verluste ohne Absorptionsspitzen über den genannten Spektralbereich gewährleisten den erfolgreichen Einsatz von PIR-Fasern für ein breites Spektrum von Anwendungen.

Für weitere Informationen besuchen Sie bitte unseren "Downloads" Bereich und finden Sie entsprechende Artikel auf unserer "Publikationen" Seite.

Spezifikationen

Specification
Core/cladding composition AgCl:AgBr
Spectral Range 3 – 17 μm
Core Refractive Index 2.15
Fresnel Reflection Losses for two surfaces 25%
Attenuation at 10.6 µm 0.2 – 0.4 dB/m
Effective Numerical Aperture NA 0.3 +/- 0.03
Melting Point 410 °C
Operating Temperature –273 to +140°C
Core/Clad Diameter (standard) see Parameters of standard Polycrystalline fibers
Laser Damage Threshold for CW CO2laser >12 kW/cm²
Tensile Strength > 70 MPa
Minimum Bending Radius (fixed) 5 x [Fiber Diameter]
Minimum Elastic Bending Radius 150 x [Fiber Diameter]
Parameters of standard Polycrystalline fibers
Code Type Core Dia., µm Cladding Dia., µm Protective Jacket Dia., µm NA Min. bending  Radius, mm
PIR240/300 Step Index Multimode 240±15 300+0/-15 no 0.30±0.03 45
PIR400/500 Step Index Multimode 410±15 500+0/-15 no 0.30±0.03 75
PIR600/700 Step Index Multimode 600±20 700+0/-15 no 0.30±0.03 100
PIR900/1000 Step Index Multimode 860±20 1000+0/-25 no 0.30±0.03 150

Downloads

PDF file   art photonics - MID-IR Polycrystalline Fiber - Flyer
PDF file   art photonics - PIR Fiber- Handling Instruction
PDF file   art photonics - MSDS_Polycrystalline Fiber
PDF file   art photonics - MID-IR Polycrystalline fiber - Datasheet

Grafiken

Anwendungen

  • Mittlere IR-Spektroskopie
  • Flexible IR-Pyrometrie
  • Flexible IR-Bildgebungssysteme
  • Leistungsübertragung für Quantenkaskadenlaser
  • Leistungsabgabe für CO- und CO2-Laser

Anfrage

Haben Sie Fragen zu diesem oder einem anderen Produkt? Senden Sie uns eine Anfrage, und unser Personal wird Ihre Frage so schnell wie möglich beantworten.

Related products

linkedin facebook pinterest youtube rss twitter instagram facebook-blank rss-blank linkedin-blank pinterest youtube twitter instagram
Copy link
CopyCopied
Powered by Social Snap