art photonics, broad spectra fiber solutions

FlexiSpec®

Spectroscopy Fiber Probes & Probe Couplers

FlexiRay®

Fibers | Cables | Bundles | Accessories

FlexiService

Loan & Installation | Measurements Training | Repair | Development
News
Latest News
Latest Events
Resources
About Our Company
art photonics GmbH, founded in Berlin in September 1998, is one of the worldwide leaders in development and production of specialty fiber products for a broad spectrum from 300 nm to 16 µm. Unique technologies of Polycrystalline Mid InfraRed (PIR-) fibers and Metal coated Silica fibers are used for assembly of various spectroscopy probes for medical diagnostics and industrial process control, in volume production of fiber for medical and industrial lasers, for different fiber bundles, etc.
UV 200-400 nm
Visible
Near IR 750-2500 nm
Mid IR 2.5 - 18 µm

Aluminiumbeschichtete Quarzglasfasern

Kategorien: , Schlagwörter: , ,

Eigenschaften:

  • Arbeitstemperaturen bis zu 400°C
  • Ausgezeichnete mechanische Festigkeit und Flexibilität
  • Keine Ausgasung unter Hochvakuumbedingungen
  • Effektive Wärmeableitung entlang der Metallbeschichtung
  • Dampf-, ETO-, Dampf-, E-Beam- oder Gamma-Sterilisierbar

Beschreibung

Die aluminiumbeschichteten Quarzglasfasern von art photonics sind die optimale Lösung für Anwendungen bei hohen Temperaturen, im Vakuum und unter rauen Umgebungsbedingungen.

Al-beschichtete Fasern haben alle Vorteile von Silica-Silica-Fasern. Zu den zusätzlichen Vorteilen gehören eine höhere mechanische Festigkeit und eine bessere Ermüdungsbeständigkeit im Vergleich zu polymerbeschichteten Fasern.

Der Transmissionsbereich reicht von 220 bis 2400 nm, je nach Wahl des UV- oder NIR-Silica-Faserkerns. Der Arbeitstemperaturbereich reicht von -270°C bis 400°C; Luftfeuchtigkeit - bis zu 100%.

Für weitere Informationen besuchen Sie bitte unseren "Downloads"-Bereich und finden Sie entsprechende Artikel auf unserer "Publikationen"-Seite.

Spezifikationen

Specification
Core/ Cladding material Step Index Pure Fused Silica Core / Fluorine Doped Silica Cladding
Graded Index Germanium Doped Fused Silica Core / Pure Fused Silica
Fiber core diameters, μm 9; 50; 62.5; 100; 200; 400; 600
Al coating thickness, μm 15 – 150 (depending on fiber diameter)
Standard Numerical Aperture (NA) 0.22 ± 0.02
Available Numerical Aperture (NA) 0.12 ± 0.02 | 0.26 ± 0.02
Min operating temperature, °C -270
Max operating temperature, °C 400
Humidity Range Up to 100%
Minimal bending radius (long term) 200 x fiber outer diameter
Minimal bending radius (short term) 100 x fiber outer diameter
Tensile strength (short gauge), GPa 3.5 – 6
Two point bending strength, GPa >10
Static fatigue parameter >100
Parameters of standard Al-coated fibers
Code Type Core, μm Cladding, μm Coating AI, μm NA
100/110 Al Step Index Multimode 100 ± 2 110 ± 2.2 140 ± 7 0.22
200/220 Al Step Index Multimode 200 ± 4 220 ± 4.4 300 ± 15 0.22
400/440 Al Step Index Multimode 400 ± 8 440 ± 8.8 560 ± 28 0.22
600/660 Al Step Index Multimode 600 ± 12 660 ± 13.2 825 ± 41.25 0.22
50/125 Al Graded Index Multimode 50 ± 1 125 ± 2.5 165 ± 3.3 0.22
9/125 Al Step Index Single Mode 9 ± 0.45 125 ± 6.25 160 ± 3.2 0.13

Downloads

Grafiken

 

Anwendungen

  • Umgebung mit hohen Temperaturen
  • Raue chemische Umgebung
  • Gegen nukleare Strahlung resistente Geräte
  • Bohrlochsensorik für die Öl- und Gasindustrie
  • Laser mit hoher Leistung
  • Medizinische Anwendungen

Anfrage

Haben Sie Fragen zu diesem oder einem anderen Produkt? Senden Sie uns eine Anfrage, und unser Personal wird Ihre Frage so schnell wie möglich beantworten.

linkedin facebook pinterest youtube rss twitter instagram facebook-blank rss-blank linkedin-blank pinterest youtube twitter instagram
Copy link
Powered by Social Snap