art photonics GmbH, founded in Berlin in September 1998, is one of the worldwide leaders in development and production of specialty fiber products for a broad spectrum from 300 nm to 16 µm. Unique technologies of Polycrystalline Mid InfraRed (PIR-) fibers and Metal coated Silica fibers are used for assembly of various spectroscopy probes for medical diagnostics and industrial process control, in volume production of fiber for medical and industrial lasers, for different fiber bundles, etc.
UV 200-400 nm
Visible
Near IR 750-2500 nm
Mid IR 2.5 - 18 µm

Chalkogenid-Mid-IR-Fasern

Kategorien: , Schlagwort:

Eigenschaften:

  • Hoher Transmissionsgrad im Bereich 1,1 - 6,5 μm
  • Geringe optische Verluste von etwa 0,2 - 0,3 dB/m bei 2,5 - 4 µm und 4,5 - 5 µm
  • Kern/Clad-Struktur mit Kerndurchmessern von 8 bis 500 μm
  • Doppelte Polymerbeschichtung für hohe Flexibilität

Weitere Informationen finden Sie in den unten aufgeführten Daten und Downloads.

Beschreibung

Chalkogenid-As-S-Glasfaser überträgt IR-Strahlung im Spektralbereich von 1,1 - 6,5μm. Hochleistungs-CIR-Kern/Mantel-Fasern werden mit Kerndurchmessern von 8µm bis 500µm gezogen.

Das fortschrittliche Ziehverfahren mit doppeltem Polymermantel sorgt für eine hervorragende mechanische Festigkeit und hohe Flexibilität der CIR-Fasern.

Niedrige optische Verluste und geringe Absorptionsspitzen über den genannten Spektralbereich gewährleisten einen erfolgreichen Einsatz von CIR-Fasern für eine Vielzahl von Anwendungen.

Für weitere Informationen besuchen Sie bitte unsere "Downloads" Sektion und finden Sie entsprechende Artikel auf unserer "Publikationen" Seite.

Spezifikationen

Specification
Core/cladding composition
As2S3
Spectral Range 1.1 – 6.5 μm
Core Refractive Index 2.42
Fresnel Reflection Losses 31%
Attenuation at 3 – 4 μm & 4.5 µm – 5 µm 0.2 – 0.4 dB/m
Effective Numerical Aperture NA see Parameters of standard Chalcogenide fibers
Glass Transition Temperature, Tg 185 °C
Operating Temperature –273°C to +90°C
Core/Clad Diameter (standard) see Parameters of standard Chalcogenide fibers
Protective Jacket Fluoro polymer + PVC
Tensile Strength > 70 MPa
Minimum Bending Radius (fixed) 100x [Fiber Diameter]
Minimum Elastic Bending Radius 200x [Fiber Diameter]
Parameters of standard Chalcogenide fibers
Code Type Core, µm Cladding, µm Protective Jacket, µm NA Min. bending Radius, mm
CIR8/300 Step Index Singlemode 8 ± 1 300 ± 15 400 ± 20 0.25 ± 0.02 60
CIR50/250 Step Index Few-mode 50 ± 3 250 ± 10  410 ± 20 0.13 ± 0.02 50
CIR250/300 Step Index Multimode 250 ± 10 300 ± 15  400 ± 30  0.30 ± 0.03 60
CIR340/400  Step Index Multimode 340 ± 10 400 ± 15 510 ± 30 0.30 ± 0.03 80
CIR500/550 Step Index Multimode 500 ± 10 550 ± 15 700 ± 30 0.30 ± 0.03 100

Downloads

PDF file   art photonics - Manual CIR-Fiber Handling Instrustion
PDF file   art photonics - MSDS Chalcogenide Fiber
PDF file   art photonics - MID-IR Chalcogenide Fiber - Datasheet

Grafiken

Anwendungen

  • Mittlere IR-Spektroskopie
  • Flexible IR-Pyrometrie
  • Flexible IR-Bildgebungssysteme
  • Leistungsabgabe für Quantenkaskadenlaser

Anfrage

Haben Sie Fragen zu diesem oder einem anderen Produkt? Senden Sie uns eine Anfrage, und unser Personal wird Ihre Frage so schnell wie möglich beantworten.